Technical Data

TYPE : TWO PACK PART A, PART B

STATE : PASTE

MIXING RATIO : FOUR PARTS OF PART A BY WHIGHT ONE PART OF PART B WEIGHT

POT LIFE : 45 MINUTES AT 30°C

THICKNESS : MAXIMUM OF 6MM

SPREADING RATE : 3000 SQ.CM/KG./1MM

CURE TIME : TOUCH HARDENING 6 HOURS

HANDLING : 12 HOURS

THROUGH HARD : 24 HOURS

FINAL RIGID : 7 DAYS

OVER COAT TIME : WITHIN 4 HOURS

MIXED DENSITY : 2.35 GM./C.CM.

COMPRESSIVE LOAD:10,000PSI(700 KG/SQ.CM)

FLEXURAL LOAD : 10,000PSI(700 KG/SQ.CM)

SHEAR ADHESION : 3000PSI (210 KG./SQ.CM)

HEAT RESISTANCE:400°C

IZODIMPACT : 45J/M

CHEMICALRESIST : DILUTE INORGANIC ACIDS, ALKALI AND SALT EXECELLENT

SHELF LIFE : BEST RESULT WITH IN ONE YEAR OF MFR. DATE